Source: Groupe CTT Group
- Before aging: 14 MPa
- After aging: 14MPa
The minimum standards for latex gloves are as follows:
- Before aging: 18 MPa
- After aging: 14MPa
ASTM has set a higher 'before aging' minimum standard for latex gloves (versus nitrile gloves) likely because latex is less durable than nitrile.
In case you didn't know: aging is the process of simulating a glove's physical condition at the end of its shelf life by placing it in a heating chamber (per ASTM D573). This is otherwise known as 'accelerated aging'. The 'accelerated aging' for exam gloves is 166 hours at 70°C, or otherwise 24 hours at 100°C. However, when stored properly, mostly gloves will not lose strength to the extent shown in 'after aging' test results.
As a buyer or user of disposable gloves, you may refer to the specification sheet of a glove in order to learn about its tensile strength.
Above is the specification table for Synguard Exam Grade Nitrile Gloves (SKU: NGPF7002). Synguard is a brand belonging to INTCO Medical, one of the world's leading manufacturers of disposable gloves. As shown above, the tensile strength of Synguard is 14 MPa before and after 'accelerated aging', which meets the ASTM D6319 standards for nitrile examination/medical gloves.
Keep in mind that while exhibiting an MPa at or above minimum standards is important, a glove should not possess too much strength, otherwise it may be difficult to don or use.
RELEVANT ASTM DOCUMENTS FOR REFERENCE:
D6319 - Standard Specification for Nitrile Examination Gloves for Medical Application
D412 - Test Methods for Vulcanized Rubber and Thermoplastic Elastomers - Tension
D573 - Test Method for Rubber - Deterioration in an Air Oven
D3767 - Practice for Rubber - Measurement of Dimensions
D5151 - Test Method for Detection of Holes in Medical Gloves
D5712 - Test Method for Analysis of Aqueous Extractable Protein in Latex, Natural Rubber, and Elastomeric Products Using the Modified Lowry Method
D6124 - Test Method for Residual Powder on Medical Gloves
D6499 - Test Method for Immunological Measurement of Antigenic Protein in Hevea Natural Rubber (HNR) and its Products